| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.60到1.75 g/cm³ |
| Apparent density | | ISO60 | 0.60到0.80 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.60到0.80 % |
| Water absorption rate | | ISO62 | <0.50 % |
| PostShrinkage | | ISO2577 | 0.10到0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO527-2 | 5000到7000 MPa |
| Tensile stress | Injection | ISO527-2 | 50.0到70.0 MPa |
| Flexural modulus | Injection | ISO178 | 7000到9000 MPa |
| Bending stress | Injection | ISO178 | 100到120 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 2.0到4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 6.0到9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 0.60到0.80 |
| Dissipation Factor | | IEC60250 | 0.040到0.060 |
| arc resistance | | ASTMD495 | PLC 5 |
| CTI | | IEC60112 | >275 V |
| Surface Resistivity | | IEC60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC60093 | 1.0E+12到1.0E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 20到30 kV/mm |
| | IEC60250 | 10.012.0 |
| | IEC60250 | 4.006.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | 160到180 °C |
| thermal conductivity | | ASTME1461 | 0.40到0.60 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.