PE Copolymer LITEN RL 58
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 0.950 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 3.0 g/10min | |
| ISO 1133 | 11 g/10min | ||
| Shrinkage rate | ISO 294-4 | 1.6 % | |
| ISO 294-4 | 3.6 % | ||
| Environmental stress cracking resistance | ISO 22088 | 18.0 hr | |
| Melt flow ratio | 25.0 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 58 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 5.5 kJ/m² | |
| ISO 179 | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile creep modulus | ISO 899-1 | 446 MPa | |
| ISO 899-1 | 262 MPa | ||
| Flexural modulus | ISO 178 | 800 MPa | |
| Tensile modulus | ISO 527-2 | 900 MPa | |
| tensile strength | Yield | ISO 527-2 | 20.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 10 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 42.0 °C | |
| melting temperature | ISO 11357-3 | 132 °C | |
| vicat | ISO 306 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.