PE Copolymer LITEN RL 58 Unipetrol RPA, s.r.o.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN RL 58 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 15 kJ/m² |
| -30°C | ISO 179 | 5.5 kJ/m² |
| hardness | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN RL 58 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 58 |
| Mechanical properties | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN RL 58 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 900 MPa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 446 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 10 % |
| tensile strength | 屈服 | ISO 527-2 | 20.0 MPa |
| Flexural modulus | ISO 178 | 800 MPa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 262 MPa |
| physical property | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN RL 58 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 0.950 g/cm³ |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 11 g/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.6 % |
| MD | ISO 294-4 | 3.6 % | |
| Environmental stress cracking resistance | 55°C,F50 | ISO 22088 | 18.0 hr |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Melt flow ratio | 21,6/2,16 | 25.0 |
| Thermal performance | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN RL 58 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 132 °C | |
| vicat | ISO 306 | 125 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 42.0 °C |