PI, TP XH1015 resin
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.31 g/cm³ | |
| ISO 1183 | 1.31 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| Melt volume flow rate | ISO 1133 | 0.00 cm³/10min | |
| Shrinkage rate | 内部方法 | 1.0to1.2 % | |
| Water absorption rate | ASTM D570 | 0.60 % | |
| ISO 62 | 2.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3420 MPa | |
| ISO 527-2/1 | 3100 MPa | ||
| tensile strength | Yield | ASTM D638 | 103 MPa |
| Yield | ISO 527-2/5 | 101 MPa | |
| ASTM D638 | 96.0 MPa | ||
| Break | ISO 527-2/5 | 74.0 MPa | |
| elongation | Yield | ASTM D638 | 7.0 % |
| bending strength | ASTM D790 | 168 MPa | |
| Tensile strain | Yield | ISO 527-2/5 | 6.0 % |
| elongation | Break | ASTM D638 | 10 % |
| Tensile strain | Break | ISO 527-2/5 | 7.0 % |
| Flexural modulus | ASTM D790 | 3130 MPa | |
| ISO 178 | 2870 MPa | ||
| bending strength | ISO 178 | 120 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 43 J/m | |
| ISO 180/1A | 4.2 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 250 °C | |
| ASTM D648 | 235 °C | ||
| ASTM D648 | 237 °C | ||
| ISO 75-2/Af | 224 °C | ||
| vicat | ASTM D152510 | 260 °C | |
| ISO 306/B50 | 250 °C | ||
| ISO 306/B120 | 248 °C | ||
| Linear coefficient of thermal expansion | ISO 11359-2 | 5E-05 cm/cm/°C | |
| ISO 11359-2 | 5.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.