PI, TP XH1015 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/XH1015 resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 43 J/m |
| 23°C | ISO 180/1A | 4.2 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/XH1015 resin |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 101 MPa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 6.0 % |
| tensile strength | 屈服 | ASTM D638 | 103 MPa |
| Break | ASTM D638 | 96.0 MPa | |
| Flexural modulus | ISO 178 | 2870 MPa | |
| bending strength | ISO 178 | 120 MPa | |
| elongation | 断裂 | ASTM D638 | 10 % |
| tensile strength | 断裂 | ISO 527-2/5 | 74.0 MPa |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 3130 MPa |
| Tensile modulus | ASTM D638 | 3420 MPa | |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 168 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 7.0 % |
| Tensile modulus | ISO 527-2/1 | 3100 MPa |
| flammability | Test Condition | Test Method | SABIC/XH1015 resin |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC/XH1015 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.0to1.2 % |
| melt mass-flow rate | 367°C/6.6kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.60 % |
| 饱和,23°C | ISO 62 | 2.3 % | |
| density | ASTM D792 | 1.31 g/cm³ | |
| ISO 1183 | 1.31 g/cm³ | ||
| Melt volume flow rate | 220°C/5.0kg | ISO 1133 | 0.00 cm³/10min |
| Thermal performance | Test Condition | Test Method | SABIC/XH1015 resin |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 237 °C |
| vicat | -- | ISO 306/B120 | 248 °C |
| Linear coefficient of thermal expansion | TD：23to150°C | ISO 11359-2 | 5.1E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 250 °C |
| vicat | -- | ISO 306/B50 | 250 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 224 °C |
| vicat | ASTM D152510 | 260 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 235 °C |
| Linear coefficient of thermal expansion | MD：23到150°C | ISO 11359-2 | 5E-05 cm/cm/°C |