PUR-Ether//TDI 442
0
CompareTechnical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| STORAGE STABILITY | 2.0 min | ||
| stripping time | 15 min | ||
| Post curing time | 16 hr | ||
| 16 hr | |||
| STORAGE STABILITY | 4.0到6.0 min | ||
| stripping time | 30 min | ||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 2.8 min | ||
| stripping time | 15 min | ||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 2.5到3.0 min | ||
| stripping time | 10 min | ||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 3.0 min | ||
| stripping time | 20 min | ||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 8.0到11 min | ||
| stripping time | 30 min | ||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 7.0到9.0 min | ||
| stripping time | 25 min | ||
| Post curing time | 4.0 hr | ||
| STORAGE STABILITY | 7.0到8.0 min | ||
| stripping time | 25 min | ||
| Post curing time | 4.0 hr | ||
| STORAGE STABILITY | 2.0到3.0 min | ||
| stripping time | 20 min | ||
| 40 min | |||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 2.8 min | ||
| stripping time | 15 min | ||
| Post curing time | 16 hr | ||
| STORAGE STABILITY | 10到12 min |
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD1505 | 1.07 g/cm³ | |
| Shrinkage rate | ASTMD955 | 1.3 % | |
| density | ASTMD1505 | 1.19 g/cm³ | |
| ASTMD1505 | 1.16 g/cm³ | ||
| Shrinkage rate | ASTMD955 | 1.1 % | |
| density | ASTMD1505 | 1.13 g/cm³ | |
| ASTMD1505 | 1.20 g/cm³ | ||
| ASTMD1505 | 1.16 g/cm³ | ||
| ASTMD1505 | 1.12 g/cm³ | ||
| Shrinkage rate | ASTMD955 | 1.3 % | |
| density | ASTMD1505 | 1.11 g/cm³ | |
| Shrinkage rate | ASTMD955 | 1.5 % | |
| density | ASTMD1505 | 1.17 g/cm³ | |
| Shrinkage rate | ASTMD955 | 1.2 % | |
| density | ASTMD1505 | 1.14 g/cm³ | |
| ASTMD1505 | 1.12 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore A | ASTMD2240 | 84 | |
| ASTMD2240 | 76 | ||
| ASTMD2240 | 70 | ||
| Shore A | ASTMD2240 | 95 | |
| ASTMD2240 | 65 | ||
| ASTMD2240 | 75 | ||
| ASTMD2240 | 66 | ||
| Shore A | ASTMD2240 | 83 | |
| Shore A | ASTMD2240 | 86 | |
| ASTMD2240 | 61 | ||
| Shore A | ASTMD2240 | 80 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| compressive strength | ASTMD695 | 0.421 MPa | |
| ASTMD695 | 1.10 MPa | ||
| ASTMD695 | 1.94 MPa | ||
| ASTMD695 | 3.17 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTMD412 | 49.6 MPa |
| elongation | Break | ASTMD412 | 250 % |
| compression set | ASTMD395B | 30 % | |
| Basho elasticity | ASTMD2632 | 55 % | |
| Tensile stress | ASTMD412 | 39.3 MPa | |
| ASTMD412 | 26.5 MPa | ||
| tensile strength | Yield | ASTMD412 | 50.3 MPa |
| elongation | Break | ASTMD412 | 260 % |
| Break | ASTMD412 | 400 % | |
| compression set | ASTMD395B | 30 % | |
| Basho elasticity | ASTMD2632 | 44 % | |
| elongation | Break | ASTMD412 | 310 % |
| compression set | ASTMD395B | 21 % | |
| Basho elasticity | ASTMD2632 | 50 % | |
| Tensile stress | ASTMD412 | 13.8 MPa | |
| ASTMD412 | 29.3 MPa | ||
| tensile strength | Yield | ASTMD412 | 51.0 MPa |
| Tensile stress | ASTMD412 | 24.8 MPa | |
| ASTMD412 | 38.6 MPa | ||
| tensile strength | Yield | ASTMD412 | 51.0 MPa |
| elongation | Break | ASTMD412 | 260 % |
| Basho elasticity | ASTMD2632 | 58 % | |
| Tensile stress | ASTMD412 | 25.5 MPa | |
| tensile strength | Yield | ASTMD412 | 34.5 MPa |
| elongation | Break | ASTMD412 | 280 % |
| Basho elasticity | ASTMD2632 | 60 % | |
| ASTMD2632 | 56 % | ||
| Tensile stress | ASTMD412 | 3.76 MPa | |
| ASTMD412 | 9.65 MPa | ||
| tensile strength | Yield | ASTMD412 | 17.2 MPa |
| elongation | Break | ASTMD412 | 400 % |
| compression set | ASTMD395B | 29 % | |
| Basho elasticity | ASTMD2632 | 30 % | |
| Tensile stress | ASTMD412 | 31.7 MPa | |
| tensile strength | Yield | ASTMD412 | 44.1 MPa |
| elongation | Break | ASTMD412 | 240 % |
| compression set | ASTMD395B | 42 % | |
| Basho elasticity | ASTMD2632 | 48 % | |
| Tensile stress | ASTMD412 | 4.48 MPa | |
| ASTMD412 | 6.21 MPa | ||
| ASTMD412 | 15.2 MPa | ||
| tensile strength | Yield | ASTMD412 | 23.4 MPa |
| elongation | Break | ASTMD412 | 400 % |
| compression set | ASTMD395B | 30 % | |
| Basho elasticity | ASTMD2632 | 30 % | |
| compression set | ASTMD395B | 36 % | |
| Basho elasticity | ASTMD2632 | 58 % | |
| Tensile stress | ASTMD412 | 21.1 MPa | |
| ASTMD412 | 46.7 MPa | ||
| tensile strength | Yield | ASTMD412 | 51.0 MPa |
| Tensile stress | ASTMD412 | 7.96 MPa | |
| tensile strength | Yield | ASTMD412 | 14.8 MPa |
| elongation | Break | ASTMD412 | 420 % |
| compression set | ASTMD395B | 34 % | |
| Basho elasticity | ASTMD2632 | 20 % | |
| Tensile stress | ASTMD412 | 4.69 MPa | |
| ASTMD412 | 8.27 MPa | ||
| tensile strength | Yield | ASTMD412 | 31.7 MPa |
| elongation | Break | ASTMD412 | 550 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.