PC PC-ABSCOM™ B300

Usages:
Shell
safety equipment
automotive interior parts
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ISO 62	0.70 %
Water absorption rate	Water absorption rate		ISO 62	0.22 %
melt mass-flow rate		ISO 1133	18 g/10min
Shrinkage rate		ISO 294-4	0.40to0.70 %
density		ISO 1183	1.15 g/cm³

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2100 MPa
tensile strength	Yield	ISO 527-2/50	50.0 MPa
	tensile strength		ISO 527-2	63.0 MPa
	tensile strength	tensile strength		ISO 527-2	20.0 MPa
Tensile strain	Break	ISO 527-2	35 %
Flexural modulus		ISO 178	2200 MPa
bending strength		ISO 178	66.0 MPa
Tensile strain	Yield	ISO 527-2/50	4.3 %
Tensile strain	Tensile strain		ISO 527-2	6.3 %

Impact resistance	Test Method	Test Result
Charpy Notched Impact Strength	ISO 179	47 kJ/m²
Impact strength of simply supported beam without notch	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	ISO 180/1A	48 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	131 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/Ae	110 °C
vicat		ISO 306/B50	130 °C
Linear coefficient of thermal expansion		ISO 11359-2	9.5E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.