PC PC-ABSCOM™ B300 Polymer Compounders Limited
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Compounders Limited/PC-ABSCOM™ B300 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 47 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 48 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Polymer Compounders Limited/PC-ABSCOM™ B300 |
|---|---|---|---|
| tensile strength | 屈服,80°C | ISO 527-2 | 20.0 MPa |
| Flexural modulus | 23°C | ISO 178 | 2200 MPa |
| tensile strength | 屈服,-40°C | ISO 527-2 | 63.0 MPa |
| Tensile strain | 屈服,-20°C | ISO 527-2 | 6.3 % |
| 断裂 | ISO 527-2 | 35 % | |
| Tensile modulus | ISO 527-2/1 | 2100 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.3 % |
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 MPa |
| bending strength | ISO 178 | 66.0 MPa |
| flammability | Test Condition | Test Method | Polymer Compounders Limited/PC-ABSCOM™ B300 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Polymer Compounders Limited/PC-ABSCOM™ B300 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40to0.70 % | |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 18 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.22 % |
| 饱和,23°C | ISO 62 | 0.70 % | |
| density | ISO 1183 | 1.15 g/cm³ |
| Thermal performance | Test Condition | Test Method | Polymer Compounders Limited/PC-ABSCOM™ B300 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 131 °C |
| vicat | ISO 306/B50 | 130 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9.5E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Ae | 110 °C |