Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.49 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.22 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 77 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 4070 MPa |
| tensile strength | Yield | ASTM D638 | 27.0 MPa |
| tensile strength | Break | ASTM D638 | 26.0 MPa |
| elongation | Yield | ASTM D638 | 1.4 % |
| elongation | Break | ASTM D638 | 1.4 % |
| Flexural modulus | | ASTM D790 | 3110 MPa |
| bending strength | Break | ASTM D790 | 37.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 41 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 120 J/m |
| Dart impact | | ASTM D5420 | 4.50 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 3.2E+11 ohms·cm |
| dielectric strength | | ASTM D149 | 8.7 kV/mm |
| dielectric constant | | ASTM D150 | 6.27 |
| Dissipation Factor | | ASTM D150 | 0.18 |
| Surface Resistivity | | ASTM D257 | 3.2E+11 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 179 °C |
| Heat distortion temperature | | ASTM D648 | 134 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.8E-04 cm/cm/°C |
| thermal conductivity | | ASTME1225 | 0.47 W/m/K |
| Specific heat capacity | | ASTME1269 | 1090 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.