EPE ELITE™ 5960G
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.962 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.85 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 14 | |
| Haze ratio | ASTM D1003 | 42 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D882 | 600 % | |
| Secant modulus | ASTM D882 | 1120 MPa | |
| ASTM D882 | 876 MPa | ||
| ASTM D882 | 1330 MPa | ||
| ASTM D882 | 1020 MPa | ||
| tensile strength | ASTM D882 | 28.3 MPa | |
| ASTM D882 | 30.3 MPa | ||
| ASTM D882 | 37.2 MPa | ||
| ASTM D882 | 24.1 MPa | ||
| elongation | ASTM D882 | 500 % | |
| film thickness | 25 µm | ||
| Thin film puncture strength | 0.339 J | ||
| 13.3 N | |||
| 内部方法 | 1.41 J/cm³ | ||
| film strength | ASTM D882 | 141 J/cm³ | |
| ASTM D882 | 128 J/cm³ | ||
| Dart impact | ASTM D1709A | 40 g | |
| Elmendorf tear strength | ASTM D1922 | 13 g | |
| ASTM D1922 | 400 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525 | 130 °C | |
| melting temperature | 内部方法 | 134 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.