Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EPE ELITE™ 5960G DOW USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW USA/ELITE™ 5960G |
|---|---|---|---|
| film strength | MD | ASTM D882 | 141 J/cm³ |
| tensile strength | TD:断裂 | ASTM D882 | 24.1 MPa |
| elongation | MD:断裂 | ASTM D882 | 500 % |
| Dart impact | ASTM D1709A | 40 g | |
| tensile strength | MD:断裂 | ASTM D882 | 37.2 MPa |
| Thin film puncture strength | 内部方法 | 1.41 J/cm³ | |
| 13.3 N | |||
| Secant modulus | 1%正割,MD | ASTM D882 | 1120 MPa |
| 2%正割,TD | ASTM D882 | 1020 MPa | |
| Thin film puncture strength | 0.339 J | ||
| Elmendorf tear strength | MD | ASTM D1922 | 13 g |
| Secant modulus | 2%正割,MD | ASTM D882 | 876 MPa |
| tensile strength | TD:屈服 | ASTM D882 | 30.3 MPa |
| Secant modulus | 1%正割,TD | ASTM D882 | 1330 MPa |
| film thickness | 25 µm | ||
| film strength | TD | ASTM D882 | 128 J/cm³ |
| Elmendorf tear strength | TD | ASTM D1922 | 400 g |
| elongation | TD:断裂 | ASTM D882 | 600 % |
| tensile strength | MD:屈服 | ASTM D882 | 28.3 MPa |
| optical performance | Test Condition | Test Method | DOW USA/ELITE™ 5960G |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 14 |
| Haze ratio | ASTM D1003 | 42 % |
| physical property | Test Condition | Test Method | DOW USA/ELITE™ 5960G |
|---|---|---|---|
| density | ASTM D792 | 0.962 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.85 g/10min |
| Thermal performance | Test Condition | Test Method | DOW USA/ELITE™ 5960G |
|---|---|---|---|
| vicat | ASTM D1525 | 130 °C | |
| melting temperature | 内部方法 | 134 °C |