| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.25 g/cm³ |
| Melt volume flow rate | | ISO1133 | 15.0 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 117 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| TristimulusValue | | ISO13468 | 0.40 % |
| TristimulusValue | | DIN5033 | 92 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2 | 12 % |
| Flexural modulus | | ISO178 | 2700 MPa |
| Bending stress | | ISO178 | 79.0 MPa |
| Tensile modulus | | ISO527-2 | 2700 MPa |
| Tensile stress | Yield | ISO527-2 | 48.0 MPa |
| Tensile stress | Break | ISO527-2 | 40.0 MPa |
| Tensile strain | Yield | ISO527-2 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 90 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B50 | 113 °C |
| | ISO75-2/A | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.