ABS AWL 113/15 WT1013-12LB ALBIS PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 90 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 11 kJ/m² |
| hardness | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 117 MPa |
| Supplementary Information | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| TristimulusValue | Y10ofTransmission:500.0µm | ISO 13468 | 0.40 % |
| Y10ofReflection | DIN 5033 | 92 % |
| Mechanical properties | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 12 % |
| Tensile modulus | ISO 527-2 | 2700 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 40.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 3.0 % |
| tensile strength | 屈服 | ISO 527-2 | 48.0 MPa |
| Flexural modulus | ISO 178 | 2700 MPa | |
| bending strength | ISO 178 | 79.0 MPa |
| flammability | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 15.0 cm³/10min |
| density | ISO 1183 | 1.25 g/cm³ |
| Thermal performance | Test Condition | Test Method | ALBIS PLASTIC GmbH/ AWL 113/15 WT1013-12LB |
|---|---|---|---|
| vicat | ISO 306/B50 | 113 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |