Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.33 g/cm³ |
| Water absorption rate | | ISO 62 | 1.9 % |
| water content | | ISO 960 | <2000 ppm |
| Water absorption rate | | ISO 62 | 1.9 % |
| density | | ISO 1183 | 1.33 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/5 | 8500 MPa |
| tensile strength | | ISO 527-2/5 | 110 MPa |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| Tensile modulus | | ISO 527-2/5 | 8500 MPa |
| tensile strength | | ISO 527-2/5 | 110 MPa |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 205 °C |
| Heat distortion temperature | | ISO 75-2/A | 195 °C |
| vicat | | ISO 306/B | 200 °C |
| melting temperature | | ISO 11357 | 223 °C |
| Heat distortion temperature | | ISO 75-2/B | 205 °C |
| Heat distortion temperature | | ISO 75-2/A | 195 °C |
| vicat | | ISO 306/B | 200 °C |
| melting temperature | | ISO 11357 | 223 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare