PA6 9B22130 I5 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 9B22130 I5 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| 23°C | ISO 180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | 4Plas/ 9B22130 I5 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 9B22130 I5 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.5 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 110 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 12 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2/5 | 8500 MPa |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 110 MPa |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| flammability | Test Condition | Test Method | 4Plas/ 9B22130 I5 |
|---|---|---|---|
| UL flame retardant rating | 3.20 mm | UL 94 | HB |
| 3.2mm | UL 94 | HB | |
| 1.60 mm | UL 94 | HB | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 650 °C |
| physical property | Test Condition | Test Method | 4Plas/ 9B22130 I5 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.9 % |
| water content | ISO 960 | <2000 ppm | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.9 % |
| density | ISO 1183 | 1.33 g/cm³ |
| Thermal performance | Test Condition | Test Method | 4Plas/ 9B22130 I5 |
|---|---|---|---|
| vicat | ISO 306/B | 200 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 205 °C |
| melting temperature | ISO 11357 | 223 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 205 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C | |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 195 °C |