PA6 SLOVAMID® 6 GF 15 LS
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 3.0 g/10min | |
| density | ISO 1183 | 1.20 g/cm³ | |
| water content | ISO 960 | 0.15 % | |
| Shrinkage rate | STM640808 | 0.67 % | |
| STM640808 | 1.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 650 °C | |
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 25 kJ/m² | |
| ISO 179 | 20 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179 | 4.0 kJ/m² | |
| ISO 179 | 3.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Yield | ISO 527-2 | 4.0 % |
| tensile strength | Yield | ISO 527-2 | 95.0 MPa |
| bending strength | ISO 178 | 150 MPa | |
| Flexural modulus | ISO 178 | 4800 MPa | |
| Tensile modulus | ISO 527-2 | 5700 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 200 °C | |
| melting temperature | ISO 3146 | 220 °C | |
| vicat | ISO 306/B | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.