Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 5.2to7.2 g/10min |
| melt mass-flow rate | | ISO 1133 | 0.20to0.26 g/10min |
| Environmental stress cracking resistance | | ISO 16770 | 400 hr |
| Melt flow ratio | | | 25.0to31.0 |
| density | | ISO 1183 | 0.947to0.951 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 62 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ResistancetoInternalPressure-HydrostaticStrength | | ISO 1167 | >2 yr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 850 MPa |
| tensile strength | Yield | ISO 527-2/50 | 23.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 36.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 10 % |
| Tensile strain | Break | ISO 527-2/50 | >1000 % |
| ResistancetoSlowCrackGrowth-NotchTest | | ISO 13479 | >1000 hr |
| Resistant to rapid crack propagation, Pc-TestS | | ISO 13477 | >20.0 bar |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 25 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B50 | 74.0 °C |
| brittle temperature | | ASTM D746 | <-80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.