HDPE SNOLEN® EP 0.26/51 N JSC Gazprom neftekhim Salavat
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EP 0.26/51 N |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 25 kJ/m² |
| Supplementary Information | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EP 0.26/51 N |
|---|---|---|---|
| ResistancetoInternalPressure-HydrostaticStrength | 80°C | ISO 1167 | >2 yr |
| hardness | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EP 0.26/51 N |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 62 |
| Mechanical properties | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EP 0.26/51 N |
|---|---|---|---|
| Tensile modulus | 23°C，正割 | ISO 527-2/1 | 850 MPa |
| ResistancetoSlowCrackGrowth-NotchTest | SCG)2 | ISO 13479 | >1000 hr |
| Tensile strain | 断裂 | ISO 527-2/50 | >1000 % |
| Resistant to rapid crack propagation, Pc-TestS | ISO 13477 | >20.0 bar | |
| Tensile strain | 屈服 | ISO 527-2/50 | 10 % |
| tensile strength | 屈服 | ISO 527-2/50 | 23.0 MPa |
| 断裂 | ISO 527-2/50 | 36.0 MPa |
| physical property | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EP 0.26/51 N |
|---|---|---|---|
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 0.20to0.26 g/10min |
| density | 23°C | ISO 1183 | 0.947to0.951 g/cm³ |
| Melt flow ratio | 25.0to31.0 | ||
| Environmental stress cracking resistance | 80°C,2%Arkopal | ISO 16770 | 400 hr |
| melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 5.2to7.2 g/10min |
| Thermal performance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EP 0.26/51 N |
|---|---|---|---|
| brittle temperature | 字段1_文本 | ASTM D746 | <-80.0 °C |
| vicat | ISO 306/B50 | 74.0 °C |