Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.15 % |
| Water absorption rate | | ASTM D570 | 0.32 % |
| Water absorption rate | | ISO 62 | 0.32 % |
| density | | ASTM D792 | 1.20 g/cm³ |
| density | | ISO 1183/B | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 3.5 g/10min |
| melt mass-flow rate | | ISO 1133 | 3.5 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 74 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/50 | 150 % |
| Flexural modulus | | ASTM D790 | 2410 MPa |
| Flexural modulus | | ISO 178 | 2410 MPa |
| bending strength | | ASTM D790 | 96.5 MPa |
| bending strength | | ISO 178 | 96.0 MPa |
| Taber abraser | | ASTM D1044 | 45 % |
| Tensile modulus | | ASTM D638 | 2480 MPa |
| Tensile modulus | | ISO 527-2/50 | 2480 MPa |
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| tensile strength | Break | ASTM D638 | 72.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 72.4 MPa |
| elongation | Break | ASTM D638 | 150 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| InstrumentedDartImpact | | ASTM D3763 | 93.8 J |
| Impact strength of cantilever beam gap | | | 630 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 960 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 93 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | NoBreak |
| Suspended wall beam without notch impact strength | | ISO 180 | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 146 °C |
| Heat distortion temperature | | ISO 75-2/B | 146 °C |
| Heat distortion temperature | | ASTM D648 | 132 °C |
| Heat distortion temperature | | ISO 75-2/A | 132 °C |
| Heat distortion temperature | | ASTM D648 | 143 °C |
| Heat distortion temperature | | ISO 75-2/A | 143 °C |
| vicat | | ASTM D15257 | 151 °C |
| vicat | | ISO 306/B50 | 151 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.