PC 2061-3 Trinseo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/2061-3 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 630 kJ/m² | ||
| 23°C | ASTM D256 | 960 J/m | |
| InstrumentedDartImpact | 23°C,TotalEnergy | ASTM D3763 | 93.8 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | NoBreak |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 93 kJ/m² |
| hardness | Test Condition | Test Method | Trinseo/2061-3 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 74 |
| R计秤 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | Trinseo/2061-3 |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 60.0 MPa |
| Flexural modulus | ISO 178 | 2410 MPa | |
| bending strength | ASTM D790 | 96.5 MPa | |
| ISO 178 | 96.0 MPa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| Taber abraser | ASTM D1044 | 45 % | |
| elongation | 断裂 | ASTM D638 | 150 % |
| Flexural modulus | ASTM D790 | 2410 MPa | |
| Tensile modulus | ASTM D638 | 2480 MPa | |
| tensile strength | 断裂 | ASTM D638 | 72.0 MPa |
| Tensile modulus | ISO 527-2/50 | 2480 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 150 % |
| tensile strength | 断裂 | ISO 527-2/50 | 72.4 MPa |
| flammability | Test Condition | Test Method | Trinseo/2061-3 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 3.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Trinseo/2061-3 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.15 % |
| density | ISO 1183/B | 1.20 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.32 % |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 3.5 g/10min |
| 300°C/1.2kg | ISO 1133 | 3.5 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/2061-3 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 132 °C |
| 1.8MPa,退火，HDT | ASTM D648 | 143 °C | |
| 1.8MPa,退火，HDT | ISO 75-2/A | 143 °C | |
| vicat | ISO 306/B50 | 151 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 132 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 146 °C |
| 0.45MPa,退火，HDT | ISO 75-2/B | 146 °C | |
| vicat | ASTM D15257 | 151 °C |