Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ASTMD792 | 1.16 g/cm³ |
| 密度 | | ISO1183 | 1.16 g/cm³ |
| 熔体体积流动速率 | 275°C/5.0kg | ISO1133 | 140 cm3/10min |
| 收缩率 | MD：3.18mm | | 0.80 % |
| 吸水率 | 饱和 | ASTMD570 | 8.5 % |
| 吸水率 | 饱和,23°C | ISO62 | 8.5 % |
| 吸水率 | 平衡,50%RH | ASTMD570 | 2.9 % |
| 吸水率 | 平衡,23°C,50%RH | ISO62 | 2.9 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 线性热膨胀系数 | MD | | 8E-05 cm/cm/°C |
| 线性热膨胀系数 | TD | | 9E-05 cm/cm/°C |
| RTI Elec | 0.38mm | UL746 | 110 °C |
| RTI Elec | 0.75mm | UL746 | 120 °C |
| RTI Elec | 1.5mm | UL746 | 120 °C |
| RTI Elec | 3.0mm | UL746 | 120 °C |
| RTI Imp | 0.38mm | UL746 | 65.0 °C |
| RTI Imp | 0.75mm | UL746 | 105 °C |
| RTI Imp | 1.5mm | UL746 | 105 °C |
| RTI Imp | 3.0mm | UL746 | 105 °C |
| 热变形温度 | 0.45MPa,未退火 | ASTMD648 | 224 °C |
| 热变形温度 | 1.8MPa,未退火 | ASTMD648 | 91.0 °C |
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 70.0 °C |
| 熔融峰值温度 | | ASTMD3418 | 243 °C |
| 溶融温度 | | ISO3146 | 243 °C |
| 线性热膨胀系数 | MD | ASTME831 | 4E-05 cm/cm/°C |
| RTI Str | 0.38mm | UL746 | 65.0 °C |
| RTI Str | 0.75mm | UL746 | 115 °C |
| RTI Str | 1.5mm | UL746 | 120 °C |
| RTI Str | 3.0mm | UL746 | 120 °C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 0.38mm | UL94 | V-0 |
| UL阻燃等级 | 0.75mm | UL94 | V-0 |
| UL阻燃等级 | 1.5mm | UL94 | V-0 |
| UL阻燃等级 | 3.0mm | UL94 | V-0 |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸应力 | 屈服,23°C | ISO527-2 | 75.0 Mpa |
| 伸长率 | 屈服,23°C | ASTMD638 | 5.0 % |
| 拉伸应变 | 屈服,23°C | ISO527-2 | 4.0 % |
| 伸长率 | 断裂,23°C | ASTMD638 | 50 % |
| 标称拉伸断裂应变 | 23°C | ISO527-2 | 6.0 % |
| 弯曲模量 | 23°C | ASTMD790 | 3000 Mpa |
| 弯曲模量 | 23°C | ISO178 | 3000 Mpa |
| 拉伸模量 | 23°C | ISO527-2 | 3500 Mpa |
| 抗张强度 | 屈服,23°C | ASTMD638 | 83.0 Mpa |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| VolumeResistivity | 1.50mm | ASTMD257 | 1E+13 ohms·cm |
| 体积电阻率 | | IEC60093 | 1E+13 ohms·cm |
| 介电强度 | | IEC60243-1 | 32 KV/mm |
| 介电常数 | 1MHz | IEC60250 | 3.60 |
| 耗散因数 | 1MHz | IEC60250 | 0.020 |
| 漏电起痕指数 | | IEC60112 | 600 V |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 球压硬度 | | ISO2039-1 | 100 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 简支梁缺口冲击强度 | -30°C | ISO179 | 4.0 kJ/m² |
| 简支梁缺口冲击强度 | 23°C | ISO179 | 9.0 kJ/m² |
| 简支梁无缺口冲击强度 | 23°C | ISO179 | 80 kJ/m² |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 32 J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 43 J/m |
| 悬壁梁缺口冲击强度 | 23°C | ISO180 | 4.5 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices