Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6/66 C3U BK BASF GERMANY
Ultramid®
Electronic insulation、Electrical components
High impact resistance、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 105 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTMD648 | 91.0 °C |
| Melting temperature (DSC) | ISO3146 | 243 °C | |
| RTIStr | 0.75mm | UL746 | 115 °C |
| Evolution Calendar intelligent importer | 3.0mm | UL746 | 105 °C |
| RTIStr | 1.5mm | UL746 | 120 °C |
| Evolution Calendar intelligent importer | 0.38mm | UL746 | 65.0 °C |
| RTIElec | 3.0mm | UL746 | 120 °C |
| RTIStr | 3.0mm | UL746 | 120 °C |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 105 °C |
| Peak Melting Temperature | ASTMD3418 | 243 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTMD648 | 224 °C |
| Linear thermal expansion coefficient | MD | 8E-05 cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 120 °C |
| 0.75mm | UL746 | 120 °C | |
| Linear thermal expansion coefficient | TD | 9E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 70.0 °C |
| Linear thermal expansion coefficient | MD | ASTME831 | 4E-05 cm/cm/°C |
| RTIElec | 0.38mm | UL746 | 110 °C |
| RTIStr | 0.38mm | UL746 | 65.0 °C |
| Hardness | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 100 Mpa |
| Physical | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.16 g/cm³ | |
| Moisture Absorption | 平衡,50%RH | ASTMD570 | 2.9 % |
| 平衡,23°C,50%RH | ISO62 | 2.9 % | |
| Modeling Shrinkage | MD：3.18mm | 0.80 % | |
| Density / Specific Gravity | ASTMD792 | 1.16 g/cm³ | |
| Melt Volume flow Rate | 275°C/5.0kg | ISO1133 | 140 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 8.5 % |
| 饱和 | ASTMD570 | 8.5 % |
| Mechanical Properties | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 6.0 % |
| Tensile Elongation | 断裂,23°C | ASTMD638 | 50 % |
| 屈服,23°C | ASTMD638 | 5.0 % | |
| Flexural Modulus | 23°C | ASTMD790 | 3000 Mpa |
| Tensile Strength | 屈服,23°C | ASTMD638 | 83.0 Mpa |
| Flexural Modulus | 23°C | ISO178 | 3000 Mpa |
| Tensile Strain | 屈服,23°C | ISO527-2 | 4.0 % |
| Tensile Stress | 屈服,23°C | ISO527-2 | 75.0 Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 3500 Mpa |
| Impact Properties | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ASTMD256 | 43 J/m |
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 80 kJ/m² |
| Notched Izod Impact Strength | -40°C | ASTMD256 | 32 J/m |
| Charpy Notched Impact Strength | 23°C | ISO179 | 9.0 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180 | 4.5 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179 | 4.0 kJ/m² |
| Flammability | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | V-0 |
| 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 | |
| 0.38mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | BASF GERMANY/C3U BK |
|---|---|---|---|
| Volume Resistivity | 1.50mm | ASTMD257 | 1E+13 ohms·cm |
| Dielectric Strength | IEC60243-1 | 32 KV/mm | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 |
| Volume Resistivity | IEC60093 | 1E+13 ohms·cm | |
| Dielectric Constant | 1MHz | IEC60250 | 3.60 |
| Comparative Tracking Index | IEC60112 | 600 V |