Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.17 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10 g/10min |
| Shrinkage rate | | 内部方法 | 0.30到0.80 % |
| Shrinkage rate | | 内部方法 | 0.10到0.30 % |
| Water absorption rate | | ISO62 | 0.10 % |
| Water absorption rate | | ISO62 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC60695-2-13 | 550 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO3451 | 17 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2/50 | 2.0 % |
| Flexural modulus | | ISO178 | 5200 MPa |
| Tensile modulus | | ISO527-2/1 | 5600 MPa |
| Tensile stress | Break | ISO527-2/50 | 78.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 60 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 96.0 °C |
| Continuous use temperature | | IEC60216 | 75.0 °C |
| BallPressure Test | | IEC60695-10-2 | 通过 |
| | ISO11359-2 | 4.5E-05 cm/cm/°C |
| vicat | | ISO306/A50 | 108 °C |
| vicat | | ISO306/B50 | 104 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.