ABS NILSAN S MR K17V Taro Plast S.p.A.
--
--
Filler, glass fiber reinforced material, 17%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 60 J/m |
Supplementary Information | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
ReinforcementContent | 750°C | ISO 3451 | 17 % |
Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
Flexural modulus | ISO 178 | 5200 MPa | |
Tensile strain | 断裂 | ISO 527-2/50 | 2.0 % |
Tensile modulus | ISO 527-2/1 | 5600 MPa | |
tensile strength | 断裂 | ISO 527-2/50 | 78.0 MPa |
Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
flammability | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
Hot filament ignition temperature | IEC 60695-2-13 | 550 °C |
physical property | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
Shrinkage rate | MD | 内部方法 | 0.10to0.30 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
饱和,23°C | ISO 62 | 0.20 % | |
Shrinkage rate | TD | 内部方法 | 0.30to0.80 % |
density | ISO 1183 | 1.17 g/cm³ | |
melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 10 g/10min |
Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./NILSAN S MR K17V |
---|---|---|---|
Continuous use temperature | IEC 60216 | 75.0 °C | |
Linear coefficient of thermal expansion | MD:-30到30°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |
vicat | -- | ISO 306/A50 | 108 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 96.0 °C |
vicat | -- | ISO 306/B50 | 104 °C |
ball-indentation hardness | 100°C | IEC 60695-10-2 | 通过 |