Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTMD792 | 1.28to1.30 g/cm³ |
melt mass-flow rate | | ASTMD1238 | 12 g/10min |
Shrinkage rate | | ASTM D955 | 0.30to0.50 % |
Water absorption rate | | ASTMD570 | 0.080 % |
Water absorption rate | Saturation | ASTM D570 | 0.25 % |
Water absorption rate | | ISO 62 | 0.25 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-1 |
Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
Limiting Oxygen Index | | ASTM D2863 | 30 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
bending strength | Break | ASTM D790 | 120 MPa |
Flexural modulus | | ASTMD790 | 4500 MPa |
bending strength | | ISO 178 | 120 MPa |
bending strength | | ISO 178 | 125 MPa |
bending strength | Yield | ASTM D790 | 125 MPa |
Tensile modulus | | ASTMD638 | 4600 MPa |
tensile strength | Yield | ASTMD638 | 80.0 MPa |
tensile strength | Break | ASTMD638 | 80.0 MPa |
elongation | Break | ASTMD638 | 5.0 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179 | 10 kJ/m² |
Impact strength of cantilever beam gap | | ASTMD256 | 110 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | ASTM D257 | >1.0E+16 ohms·cm |
dielectric strength | | ASTM D149 | 22 kV/mm |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTMD648 | 142 °C |
Continuous use temperature | | IEC 60216 | 130 °C |
vicat | | ISO 306/A50 | 153 °C |
ball-indentation hardness | | VDE0470 | 通过 |
Linear coefficient of thermal expansion | | ASTM D696 | 3.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.