PC TAROLON 2500 G3 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTaro Plast S.p.A./TAROLON 2500 G3
Charpy Notched Impact Strength23°CISO 17910 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTMD256110 J/m
Mechanical propertiesTest ConditionTest MethodTaro Plast S.p.A./TAROLON 2500 G3
Flexural modulusASTMD7904500 MPa
bending strength--2ISO 178120 MPa
elongation断裂ASTMD6385.0 %
bending strength屈服ASTM D790125 MPa
断裂ASTM D790120 MPa
Tensile modulusASTMD6384600 MPa
tensile strength 断裂ASTMD63880.0 MPa
屈服ASTMD63880.0 MPa
bending strength--3ISO 178125 MPa
Electrical performanceTest ConditionTest MethodTaro Plast S.p.A./TAROLON 2500 G3
Volume resistivityASTM D257>1.0E+16 ohms·cm
dielectric strength2.00mmASTM D14922 kV/mm
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 4
flammabilityTest ConditionTest MethodTaro Plast S.p.A./TAROLON 2500 G3
Hot filament ignition temperature2.0mmIEC 60695-2-13850 °C
UL flame retardant rating3.2mmUL 94V-1
Limiting Oxygen IndexASTM D286330 %
physical property Test ConditionTest MethodTaro Plast S.p.A./TAROLON 2500 G3
Shrinkage rateMDASTM D9550.30to0.50 %
Water absorption rate饱和ASTM D5700.25 %
densityASTMD7921.28to1.30 g/cm³
Water absorption rate23°C,24hrASTMD5700.080 %
melt mass-flow rate300°C/1.2kgASTMD123812 g/10min
Water absorption rate饱和,23°CISO 620.25 %
Thermal performanceTest ConditionTest MethodTaro Plast S.p.A./TAROLON 2500 G3
Heat distortion temperature1.8MPa,未退火，HDTASTMD648142 °C
vicatISO 306/A50153 °C
Continuous use temperatureIEC 60216130 °C
ball-indentation hardness125°CVDE0470通过
Linear coefficient of thermal expansionMD：-30到30°CASTM D6963.3E-05 cm/cm/°C