Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.919 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 1.5 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 47 |
| Shore hardness | | ISO 868 | 45 |
| ball-indentation hardness | | ISO 2039-1 | 15.0 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 75 |
| gloss | | ASTM D2457 | >20 |
| Haze ratio | | ASTM D1003 | <11 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Failure energy | | DIN 53373 | 45.0 J/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 10.8 MPa |
| tensile strength | | ISO 527-2 | 9.00 MPa |
| tensile strength | Break | ASTM D638 | 12.2 MPa |
| Tensile modulus | | ASTM D638 | 254 MPa |
| Tensile modulus | | ISO 527-2 | 200 MPa |
| Flexural modulus | | ASTM D790 | 241 MPa |
| coefficient of friction | | ISO 8295 | 0.75 |
| Tensile strain | Yield | ISO 527-2 | 15 % |
| Tensile strain | Break | ASTM D638 | 670 % |
| film | Test Condition | Test Method | Test Result |
|---|
| film thickness | | | 50 µm |
| film thickness | | | 30to80µ |
| tensile strength | | ISO 527-3 | 27.0 MPa |
| tensile strength | | ISO 527-3 | 17.0 MPa |
| elongation | | ISO 527-3 | 200 % |
| elongation | | ISO 527-3 | 600 % |
| Dart impact | | ASTM D1709 | 120 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 3146 | 108 °C |
| vicat | | ASTM D1525 | 87.0 °C |
| vicat | | ISO 306/A50 | 88.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare