Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE Purell PE 1840 H HMC Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodHMC Polymers/Purell PE 1840 H
Shore hardness邵氏DASTM D224047
ball-indentation hardnessH49/30ISO 2039-115.0 MPa
Shore hardness邵氏DISO 86845
Supplementary InformationTest ConditionTest MethodHMC Polymers/Purell PE 1840 H
Failure energy50.0µmDIN 5337345.0 J/cm
filmTest ConditionTest MethodHMC Polymers/Purell PE 1840 H
film thickness30to80µ
tensile strength TD:50µm,吹塑薄膜ISO 527-317.0 MPa
elongationMD:断裂,50µm,吹塑薄膜ISO 527-3200 %
tensile strength MD:50µm,吹塑薄膜ISO 527-327.0 MPa
film thickness50 µm
Dart impact50µmASTM D1709120 g
elongationTD:断裂,50µm,吹塑薄膜ISO 527-3600 %
Mechanical propertiesTest ConditionTest MethodHMC Polymers/Purell PE 1840 H
coefficient of frictionISO 82950.75
Tensile strain断裂ASTM D638670 %
tensile strength 屈服,23°CISO 527-29.00 MPa
Tensile modulus23°CISO 527-2200 MPa
tensile strength 断裂ASTM D63812.2 MPa
Flexural modulusASTM D790241 MPa
Tensile strain屈服ISO 527-215 %
tensile strength 屈服ASTM D63810.8 MPa
Tensile modulus1%正割ASTM D638254 MPa
optical performance Test ConditionTest MethodHMC Polymers/Purell PE 1840 H
gloss20°,50.0µm,吹塑薄膜ASTM D2457>20
Haze ratio50.0µm,吹塑薄膜ASTM D1003<11 %
gloss60°,50.0µm,吹塑薄膜ASTM D52375
physical property Test ConditionTest MethodHMC Polymers/Purell PE 1840 H
melt mass-flow rate190°C/2.16kgASTMD12381.5 g/10min
densityISO 11830.919 g/cm³
Thermal performanceTest ConditionTest MethodHMC Polymers/Purell PE 1840 H
vicat--ASTM D152587.0 °C
--ISO 306/A5088.0 °C
melting temperatureISO 3146108 °C