ABS+PBT Infino GP-3200G
0
- Properties:physical property
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 33 g/10min | |
| Shrinkage rate | ASTM D955 | 0.40to0.90 % | |
| Water absorption rate | ASTM D570 | 0.080 % | |
| ash content | ISO 3451 | 19 % | |
| ASTM D5630 | 19 % | ||
| Heat distortion temperature | ASTM D648 | 145 °C | |
| Impact strength of cantilever beam gap | ASTM D256 | 65 J/m | |
| ISO 180/1A | 7.5 kJ/m² | ||
| Rockwell hardness | R-Scale | ASTM D785 | 112 |
| R-Scale | ISO 2039-2 | 110 | |
| Heat distortion temperature | ASTM D648 | 205 °C | |
| ISO 75-2/B | 198 °C | ||
| density | ASTM D792 | 1.32 g/cm³ | |
| ISO 1183 | 1.32 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 33 g/10min | |
| bending strength | ASTM D790 | 118 MPa | |
| ISO 178 | 130 MPa | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 8.3 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 65 J/m | |
| Tensile modulus | ASTM D638 | 4900 MPa | |
| ISO 527-2/50 | 5000 MPa | ||
| tensile strength | Yield | ASTM D638 | 78.5 MPa |
| Yield | ISO 527-2/50 | 91.0 MPa | |
| Break | ASTM D638 | 78.5 MPa | |
| Break | ISO 527-2/50 | 90.0 MPa | |
| elongation | Break | ASTM D638 | 3.2 % |
| Tensile strain | Break | ISO 527-2/50 | 3.6 % |
| Flexural modulus | ASTM D790 | 4900 MPa | |
| ISO 178 | 5000 MPa | ||
| Heat distortion temperature | ISO 75-2/A | 127 °C | |
| vicat | ISO 306/B50 | 129133 °C | |
| ISO 306/B120 | 131137 °C | ||
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.