PPO(PPE)+PS+PA NORYL GTX™ GTX840 resin

0
  • Properties:
    Filler
    glass fiber reinforced material
    40%
    filler by weight
  • Usages:
    Parts under the hood of a car

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
Water absorption rateASTM D5700.30 %
Water absorption rateISO 620.10 %
densityASTMD7921.45 g/cm³
Melt volume flow rateISO 113310.0 cm³/10min
Shrinkage rate内部方法0.24to0.27 %
Shrinkage rate内部方法0.60to0.63 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785108
Mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D63813500 MPa
Tensile modulusISO 527-2/113900 MPa
tensile strength ASTM D638178 MPa
tensile strength BreakISO 527-2/5198 MPa
elongationASTM D6382.0 %
elongationBreakISO 527-2/52.0 %
Flexural modulusASTM D79011900 MPa
Flexural modulusISO 17812300 MPa
bending strengthISO 178280 MPa
bending strengthASTM D790249 MPa
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact StrengthISO 179/2C11 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA11 kJ/m²
Impact strength of cantilever beam gapASTM D25690 J/m
Impact strength of cantilever beam gapASTM D25694 J/m
Impact strength of cantilever beam gapISO 180/1A11 kJ/m²
Impact strength of cantilever beam gapISO 180/1A11 kJ/m²
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureISO 75-2/Bf258 °C
Heat distortion temperatureASTM D648247 °C
Heat distortion temperatureISO 75-2/Af244 °C
vicatISO 306/B50246 °C
Linear coefficient of thermal expansionASTME8311.6E-5到2.0E-5 cm/cm/°C
Linear coefficient of thermal expansionASTME8319.0E-5到9.4E-5 cm/cm/°C
Heat distortion temperatureASTM D648260 °C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.