Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:27 |
| Post curing time | | | 4.0 hr |
| Post curing time | | | 6.0 hr |
| Post curing time | | | 6.0 hr |
| Post curing time | | | 2.0 hr |
| Post curing time | | | 2.0 hr |
| Post curing time | | | 2.0 hr |
| Post curing time | | | 4.0 hr |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.09to1.13 g/cm³ |
| Viscosity | | | 0.30to0.50 Pa·s |
| Curing Time | | | 24to48 hr |
| STORAGE STABILITY | | | 120to150 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619 | 85to89 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 3030to3070 MPa |
| bending strength | | ISO 178 | 120to140 MPa |
| compression stress | | ISO 604 | 95.0to115 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 28to42 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 145to149 °C |
| Glass Transition Temperature | | DSC | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.