Epoxy Ebalta LH 26 / Resin+Hardener Ebalta Kunststoff GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta LH 26 / Resin+Hardener |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 28to42 kJ/m² |
| hardness | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta LH 26 / Resin+Hardener |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 7619 | 85to89 |
| Mechanical properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta LH 26 / Resin+Hardener |
|---|---|---|---|
| compression stress | ISO 604 | 95.0to115 MPa | |
| Flexural modulus | ISO 178 | 3030to3070 MPa | |
| bending strength | ISO 178 | 120to140 MPa |
| thermosetting | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta LH 26 / Resin+Hardener |
|---|---|---|---|
| Thermosetting components | 按重量计算的混合比 | 100 | |
| Post curing time | 100°C | 2.0 hr | |
| 120°C | 2.0 hr | ||
| 80°C | 6.0 hr | ||
| 60°C | 6.0 hr | ||
| 40°C | 4.0 hr | ||
| 150°C | 2.0 hr | ||
| Thermosetting components | 硬化法 | 按重量计算的混合比:27 | |
| Post curing time | 180°C | 4.0 hr |
| Uncured Properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta LH 26 / Resin+Hardener |
|---|---|---|---|
| Viscosity | 25°C | 0.30to0.50 Pa·s | |
| STORAGE STABILITY | 20°C | 120to150 min | |
| density | 20°C | 1.09to1.13 g/cm³ | |
| Curing Time | 20°C | 24to48 hr |
| Thermal performance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta LH 26 / Resin+Hardener |
|---|---|---|---|
| Glass Transition Temperature | DSC | 150 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 145to149 °C |