ASA

ASA Generic ASA+PC Generic

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C	ASTM D3763	35.3to47.9 J
Impact strength of cantilever beam gap	23°C	ISO 180	16to61 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	140to600 J/m
Charpy Notched Impact Strength	23°C	ISO 179	5.0to62 kJ/m²

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		IEC 60695-2-13	550to960 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,23°C	ISO 527-2	54.6to62.4 MPa
tensile strength	tensile strength	Yield,23°C	ASTM D638	52.9to65.6 MPa
Tensile modulus	23°C	ISO 527-2	2120to2760 MPa
Tensile modulus	Tensile modulus	23°C	ASTM D638	2540to2720 MPa
tensile strength	Break,23°C	ASTM D638	44.0to66.0 MPa
tensile strength	tensile strength	Break,23°C	ISO 527-2	39.0to64.3 MPa
elongation	Yield,23°C	ASTM D638	3.7to6.1 %
	elongation	Yield,23°C	ISO 527-2	2.3to8.7 %
		elongation	Break,23°C	ASTM D638	23to100 %
		elongation	elongation	Break,23°C	ISO 527-2	36to80 %
Bending modulus	23°C	ASTM D790	2080to2770 MPa
Bending modulus	Bending modulus	23°C	ISO 178	2000to2640 MPa
bending strength	23°C	ASTM D790	68.0to94.0 MPa
	bending strength	23°C	ISO 178	72.8to97.5 MPa
	bending strength	bending strength	Yield,23°C	ASTM D790	81.7to95.4 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	102to130 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7.1E-5到7.8E-5 cm/cm/°C
	Linear coefficient of thermal expansion	TD	ASTME831	7.2E-5到7.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.0E-5到8.6E-5 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	98.4to132 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	87.7to113 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	87.2to122 °C
Vicat softening temperature	--	ASTM D1525	104to138 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306	102to139 °C
Linear coefficient of thermal expansion	MD	ASTME831	7.2E-5到7.3E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ASTM D570	0.10to0.25 %
Shrinkage rate	23°C	ISO 294-4	0.59to0.70 %
Shrinkage rate	Shrinkage rate	MD:23°C	ASTM D955	0.50to0.60 %
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	17.0to26.0 cm³/10min
melt mass-flow rate	260°C/5.0kg	ISO 1133	19to40 g/10min
melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ASTM D1238	14to45 g/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20to0.30 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.60to1.0 %
density	--	ASTM D792	1.10to1.25 g/cm³
density	density	23°C	ISO 1183	1.11to1.20 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	23°C	IEC 60093	1.0E+13到1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1.0E+13到1.0E+15 ohms

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	88.7to110 MPa
Rockwell hardness	23°C	ASTM D785	109to116

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top