PA66 EPR32
237
- Properties:Flame retardantHigh glosshigh viscosityIlluminatedHigh viscosity products
- Usages:Fiber grade
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Terminal carboxyl content | QB | 56±3 MEQ/KG | |
| Terminal amino content | QB | 36±3 MEQ/KG | |
| Water absorption rate | GB | ≤700 ppm | |
| relative viscosity | QB | 3.20±0.01 | |
| Impurities and color particles | QB | ≤0.017 % |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 有光、高粘度产品 | ||
| purpose | 用于注塑成型挤出.还可用于不同用途的复丝挤出。作为改性基料.特别适宜于阻燃改性 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ISO 527 | 30.9 % | |
| Flexural modulus | ISO 178 | 0.9 GPa | |
| Tensile modulus | ISO 527 | 2.4 GPa | |
| Charpy Notched Impact Strength | ISO 179 | 7.9 KJ/m | |
| tensile strength | ISO 527 | 78.2 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 不断 KJ/m | |
| Impact strength of cantilever beam gap | ISO 180 | 5.4 KJ/m | |
| bending strength | ISO 178 | 73.7 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 243 | -- KV/mm | |
| Volume resistivity | IEC 93 | -- Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75 | 71.6 °C | |
| melt mass-flow rate | ISO 1133 | 3.4 g/10min | |
| Linear coefficient of thermal expansion | ASTM D696 | 7.5 | |
| melting temperature | ISO 3146 | 235-258 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.