Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 EPR32 HENAN SHENMA NYLON
--
Fiber grade
Flame retardant、High gloss、high viscosity、 Illuminated、High viscosity products
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | HENAN SHENMA NYLON/EPR32 |
|---|---|---|---|
| tensile strength | ISO 527 | 78.2 Mpa | |
| Impact strength of cantilever beam gap | ISO 180 | 5.4 KJ/m | |
| bending strength | ISO 178 | 73.7 Mpa | |
| Tensile modulus | ISO 527 | 2.4 GPa | |
| Flexural modulus | ISO 178 | 0.9 GPa | |
| elongation | 断裂 | ISO 527 | 30.9 % |
| Charpy Notched Impact Strength | ISO 179 | 不断 KJ/m |
| Electrical performance | Test Condition | Test Method | HENAN SHENMA NYLON/EPR32 |
|---|---|---|---|
| dielectric strength | IEC 243 | -- KV/mm | |
| Volume resistivity | IEC 93 | -- Ω.cm |
| other | Test Condition | Test Method | HENAN SHENMA NYLON/EPR32 |
|---|---|---|---|
| characteristic | 有光、高粘度产品 | ||
| purpose | 用于注塑成型挤出.还可用于不同用途的复丝挤出。作为改性基料.特别适宜于阻燃改性 |
| physical property | Test Condition | Test Method | HENAN SHENMA NYLON/EPR32 |
|---|---|---|---|
| Water absorption rate | 干切片 | GB | ≤700 ppm |
| Impurities and color particles | QB | ≤0.017 % | |
| Terminal carboxyl content | COOH | QB | 56±3 MEQ/KG |
| relative viscosity | QB | 3.20±0.01 | |
| Terminal amino content | QB | 36±3 MEQ/KG |
| Thermal performance | Test Condition | Test Method | HENAN SHENMA NYLON/EPR32 |
|---|---|---|---|
| Heat distortion temperature | HDT | ISO 75 | 71.6 °C |
| melt mass-flow rate | ISO 1133 | 3.4 g/10min | |
| Linear coefficient of thermal expansion | ASTM D696 | 7.5 | |
| melting temperature | ISO 3146 | 235-258 °C |