PP PPH1S07 G40

Properties:
Filler
glass fiber reinforced material
40%
filler by weight
Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO 1183/A	1.25 g/cm³
melt mass-flow rate	ISO 1133	7.0 g/10min
density	ISO 1183/A	1.25 g/cm3
melt mass-flow rate	ISO 1133	7.0 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	8800 MPa
Tensile modulus	Tensile modulus		ISO 527-2	8800 MPa
tensile strength	Break	ISO 527-2	95.0 MPa
Tensile strain	Yield	ISO 527-2	3.0 %
Flexural modulus		ISO 178	8000 MPa
tensile strength	Break	ISO 527-2	95.0 MPa
Tensile strain	Yield	ISO 527-2	3.0 %
Flexural modulus		ISO 178	8000 MPa
bending strength		ISO 178	150 MPa
Charpy Notched Impact Strength		ISO 179/1eA	10 kJ/m2
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eU	50 kJ/m2
bending strength		ISO 178	150 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	10 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	50 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	150 ℃
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	150 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.