PP PPH1S07 G40 Repol Engineering Plastics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Repol Engineering Plastics/PPH1S07 G40 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
Mechanical properties | Test Condition | Test Method | Repol Engineering Plastics/PPH1S07 G40 |
---|---|---|---|
Tensile modulus | ISO 527-2 | 8800 MPa | |
tensile strength | 断裂 | ISO 527-2 | 95.0 MPa |
Tensile strain | 屈服 | ISO 527-2 | 3.0 % |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 10 kJ/m2 |
Flexural modulus | ISO 178 | 8000 MPa | |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 50 kJ/m2 |
bending strength | ISO 178 | 150 MPa |
physical property | Test Condition | Test Method | Repol Engineering Plastics/PPH1S07 G40 |
---|---|---|---|
density | ISO 1183/A | 1.25 g/cm³ | |
melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 7.0 g/10min |
density | ISO 1183/A | 1.25 g/cm3 | |
melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 7.0 g/10min |
Thermal performance | Test Condition | Test Method | Repol Engineering Plastics/PPH1S07 G40 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 150 °C |
1.8 MPa, 未退火,HDT | ISO 75-2/A | 150 ℃ |