| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.32 % |
| Shrinkage rate | | 内部方法 | 0.13 % |
| Water absorption rate | | ASTM D570 | 0.37 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| 0.60 mm, All Colors | | | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 18500 Mpa |
| Tensile stress | | ISO 527-2 | 245 Mpa |
| Tensile strain | | ISO 527-2 | 2.3 % |
| Flexural modulus | | ISO 178 | 15900 Mpa |
| Bending stress | | ISO 178 | 379 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ISO 180 | 68 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D2520 | 4.15 |
| dielectric constant | | ASTM D2520 | 4.15 |
| Dissipation Factor | | ASTM D2520 | 0.011 |
| Dissipation Factor | | ASTM D2520 | 0.011 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| drying time | | | 4.0 到 12 hr |
| Suggested maximum moisture content | | | 0.090 % |
| Temperature at the rear of the barrel | | | 250 °C |
| Temperature at the front of the material cylinder | | | 280 °C |
| Processing (melt) temperature | | | 285 到 305 °C |
| Temperature | | | 80 到 120 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 262 °C |
| | ISO 75-2/A | 254 °C |
| melting temperature | | ASTM D3418 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.