PA66 9950 WH000 SOLVAY USA
KALIX®
Fitness equipment、Automotive Applications
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
Suspended wall beam without notch impact strength | ISO 180 | 68 kJ/m² |
Mechanical properties | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
Tensile modulus | ISO 527-2 | 18500 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 2.3 % |
Flexural modulus | ISO 178 | 15900 Mpa | |
bending strength | 3.5% 应变 | ISO 178 | 379 Mpa |
tensile strength | 屈服 | ISO 527-2 | 245 Mpa |
Electrical performance | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
Dissipation Factor | 2.40 GHz | ASTM D2520 | 0.011 |
dielectric constant | 1.00 GHz | ASTM D2520 | 4.15 |
2.40 GHz | ASTM D2520 | 4.15 | |
Dissipation Factor | 1.00 GHz | ASTM D2520 | 0.011 |
flammability | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
0.60 mm, All Colors | 0.60 mm, 所有颜色 | HB |
physical property | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.37 % |
Shrinkage rate | 横向流量 | 内部方法 | 0.32 % |
流量 | 内部方法 | 0.13 % |
Thermal performance | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
Heat distortion temperature | 0.45 MPa, 未退火,HDT | ISO 75-2/B | 262 °C |
1.8 MPa, 未退火,HDT | ISO 75-2/A | 254 °C | |
melting temperature | ASTM D3418 | 260 °C |
injection | Test Condition | Test Method | SOLVAY USA/9950 WH000 |
---|---|---|---|
drying time | 4.0 to 12 hr | ||
Suggested maximum moisture content | 0.090 % | ||
Temperature at the rear of the barrel | 250 °C | ||
Processing (melt) temperature | 285 to 305 °C | ||
drying temperature | 80 °C | ||
Temperature at the front of the material cylinder | 280 °C | ||
Temperature | 80 to 120 °C |