Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Hardener | | 按重量计算的混合比:28按容量计算的混合比:28 |
| Thermosetting components | Demold Time | | 240to360 min |
| Thermosetting components | Resin | | 按重量计算的混合比:100按容量计算的混合比:100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.08 g/cm³ |
| Shrinkage rate | | ASTM D2566 | 0.20to0.60 % |
| density | Base Resin | | 1.08 g/cm³ |
| density | | | 1.08 g/cm³ |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Viscosity | | | 0.40 Pa·s |
| Viscosity | | | 3.3 Pa·s |
| Viscosity | | | 7.1 Pa·s |
| Viscosity | | | 1.7E+02 hr |
| Viscosity | | | 20to30 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 91to99 |
| tensile strength | | ASTM D638 | 26.5 MPa |
| elongation | Break | ASTM D638 | 400 % |
| tear strength | | ASTM D624 | 81.4 kN/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Taber abraser | | ASTM D4060 | 12.0 mg |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | Split | ASTM D470 | 29 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.