PLA Luminy® L105

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Melt flow rate (melt flow rate) 2		ISO 1133	22 g/10 min
Melt flow rate (melt flow rate) 2	Melt flow rate (melt flow rate) 2		ISO 1133	50 g/10 min
water content		Karl Fisher	< 400 ppm

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	3500 Mpa
Tensile stress	ISO 527-2	50.0 Mpa
Tensile strain	ISO 527-2	< 5.0 %

injection	Test Condition	Test Method	Test Result
drying temperature			100 °C
drying time			4.0 到 6.0 hr
Dew Point			< -40 °C
Suggested maximum moisture content			0.025 %
Hopper temperature			20 到 40 °C
Temperature at the rear of the barrel			155 到 175 °C
Temperature in the middle of the barrel			180 到 220 °C
Spray nozzle temperature			180 到 220 °C
Processing (melt) temperature			180 到 220 °C
Back pressure			5.00 到 10.0 Mpa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/Bf	55.0 到 60.0 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/Bf	100 到 110 °C
Glass Transition Temperature		DSC	55.0 到 60.0 °C
melting temperature		DSC	175 °C
Monomer Residue		内部方法	< 0.30 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.