PLA L105 TOTAL THAILAND
Luminy®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | TOTAL THAILAND/L105 |
|---|---|---|---|
| Glass Transition Temperature | DSC | 55.0 to 60.0 °C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火4 | ISO 75-2/Bf | 100 to 110 °C |
| 0.45 MPa, 未退火3 | ISO 75-2/Bf | 55.0 to 60.0 °C | |
| melting temperature | DSC | 175 °C | |
| Monomer Residue | 内部方法 | < 0.30 % |
| mechanical properties | Test Condition | Test Method | TOTAL THAILAND/L105 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | < 5.0 % |
| tensile strength | ISO 527-2 | 50.0 Mpa |
| Physical properties | Test Condition | Test Method | TOTAL THAILAND/L105 |
|---|---|---|---|
| melt mass-flow rate | 210°C/2.16 kg | ISO 1133 | 50 g/10 min |
| 190°C/2.16 kg | ISO 1133 | 22 g/10 min | |
| water content | Karl Fisher | < 400 ppm |
| injection | Test Condition | Test Method | TOTAL THAILAND/L105 |
|---|---|---|---|
| Back pressure | 5.00 to 10.0 Mpa | ||
| Dew point temperature | < -40 °C | ||
| drying temperature | 100 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Hopper temperature | 20 to 40 °C | ||
| Processing (melt) temperature | 180 to 220 °C | ||
| Spray nozzle temperature | 180 to 220 °C | ||
| Suggested maximum moisture content | 0.025 % | ||
| Temperature at the rear of the barrel | 155 to 175 °C | ||
| Temperature in the middle of the barrel | 180 to 220 °C |