PA66/C/PTFE LNP™ LUBRICOMP™ RCL-4536
91
- Properties:High temperature resistanThermal stability
- Usages:Automotive componentsElectronic and electrical accessories
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.20 % | |
| ASTMD955 | 0.40 % | ||
| ISO294-4 | 0.43 % | ||
| ISO294-4 | 0.15 % | ||
| Water absorption rate | ASTMD570 | 0.93 % | |
| ISO62 | 1.4 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FlameRating | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTMD638 | 201 Mpa | |
| Tensile stress | ISO527-2 | 228 Mpa | |
| elongation | ASTMD638 | 1.4 % | |
| Tensile strain | ISO527-2 | 2.0 % | |
| Flexural modulus | ASTMD790 | 16400 Mpa | |
| ISO178 | 21300 Mpa | ||
| bending strength | ASTMD790 | 333 Mpa | |
| Bending stress | ISO178 | 354 Mpa | |
| ASTMD3702Modified | 0.25 | ||
| ASTMD3702Modified | 0.23 | ||
| Tensile modulus | ASTMD638 | 29500 Mpa | |
| ISO527-2/1 | 23100 Mpa | ||
| Wear factor - Washer | ASTMD3702Modified | 6.00 10^-10in^5-min/ft-lb-hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | ISO180/1A | 10 kJ/m² | |
| UnnotchedIzodImpactStrength3 | ISO180/1U | 65 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 9.90 J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.85 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTME831 | 2.2E-05 cm/cm/°C | ||
| ISO11359-2 | 2.3E-05 cm/cm/°C | ||
| ASTME831 | 3.4E-05 cm/cm/°C | ||
| ISO11359-2 | 3.4E-05 cm/cm/°C | ||
| ASTMD648 | 254 °C | ||
| ASTMD648 | 244 °C | ||
| Hot deformation temperature 4 | ISO75-2/Af | 245 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.