PA66/C/PTFE RCL-4536 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components、Electronic and electrical
High temperature resistan、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RCL-4536 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 65 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.85 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 9.90 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RCL-4536 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 23100 Mpa | |
| bending strength | ASTM D790 | 333 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 201 Mpa |
| 断裂 | ISO 527-2 | 228 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 6.00 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 16400 Mpa | |
| Tensile modulus | ASTM D638 | 29500 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.4 % |
| bending strength | ISO 178 | 354 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.23 |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 21300 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.25 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/RCL-4536 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/RCL-4536 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.15 % |
| MD：24小时 | ASTM D955 | 0.20 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.93 % |
| 平衡,23°C,50%RH | ISO 62 | 1.4 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.40 % |
| TD:24小时 | ISO 294-4 | 0.43 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RCL-4536 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 3.4E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 3.4E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 2.2E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 254 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 2.3E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 245 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 244 °C |