Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.45 g/10min |
| Environmental stress cracking resistance | | ASTM D1693B | 630 hr |
| density | | ISO 1183 | 0.952 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 0.10 g/10min |
| melt mass-flow rate | | ISO 1133 | 10 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 65 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Blow molding temperature | | | 190to220 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 1500 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 28 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-3 | 27.0 MPa |
| tensile strength | Break | ISO 527-3 | 37.0 MPa |
| elongation | Break | ISO 527-3 | 1400 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A120 | 128 °C |
| Oxygen induction time | | EN728 | 90 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.