HDPE TIPELIN® BS 520-14 MOL Petrochemicals Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 28 kJ/m² |
| hardness | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 65 |
| Supplementary Information | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| Blow molding temperature | 190to220 °C |
| film | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-3 | 37.0 MPa |
| 屈服 | ISO 527-3 | 27.0 MPa | |
| elongation | 断裂 | ISO 527-3 | 1400 % |
| Mechanical properties | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 1500 MPa |
| physical property | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| Environmental stress cracking resistance | 10%IgepalCO-630,F50 | ASTM D1693B | 630 hr |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 0.45 g/10min |
| density | 23°C | ISO 1183 | 0.952 g/cm³ |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.10 g/10min |
| 190°C/21.6kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 520-14 |
|---|---|---|---|
| Oxygen induction time | 200°C | EN728 | 90 min |
| vicat | ISO 306/A120 | 128 °C |