ABS Stylac™ VA58
35
- Properties:Flame retardant
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 25 g/10min | |
| Melt volume flow rate | ISO 1133 | 25.0 cm3/10min | |
| Shrinkage rate | ASTM D955 | 0.40-0.60 % | |
| melt mass-flow rate | ISO 1133 | 25 g/10 min | |
| Melt volume flow rate | ISO 1133 | 3.00 cm3/10min | |
| Shrinkage rate | ASTM D955 | 0.40-0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 46.8 Mpa | |
| Flexural modulus | ISO 178 | 2550 Mpa | |
| bending strength | ISO 178 | 78.7 Mpa | |
| tensile strength | ISO 527-2/5 | 47.0 Mpa | |
| Flexural modulus | ISO 178 | 2550 Mpa | |
| bending strength | ISO 178 | 79.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 11 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 75.7 °C | |
| vicat | ISO 306/B | 91.5 °C | |
| RTI Elec | UL 746 | 60.0 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| ball-indentation hardness | EMAC | 80 °C | |
| Heat distortion temperature | ISO 75-2/A | 76.0 °C | |
| vicat | ISO 306/B | 92.0 °C | |
| Ball pressure temperature | 80.0 °C | ||
| UL flame retardant rating | UL 94 | V-0 | |
| RTI Str | UL 746 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.