ABS VA58 ASAHI JAPAN
Stylac™
--
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/VA58 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 47.0 Mpa |
| 屈服 | ISO 527-2/50 | 46.8 Mpa | |
| bending strength | ISO 178 | 79.0 Mpa | |
| Flexural modulus | ISO 178 | 2550 Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 11 kJ/m² |
| flammability | Test Condition | Test Method | ASAHI JAPAN/VA58 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 2.1mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/VA58 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Melt volume flow rate | 220℃/10.0 kg | ISO 1133 | 3.00 cm3/10min |
| melt mass-flow rate | 220℃/10.0 kg | ISO 1133 | 25 g/10 min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 25.0 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/VA58 |
|---|---|---|---|
| vicat | ISO 306/B | 92.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.7 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 76.0 °C | |
| Ball pressure temperature | 80.0 °C | ||
| RTI Imp | UL 746 | 60.0 °C | |
| UL flame retardant rating | 2.10 mm | UL 94 | V-0 |
| RTI | UL 746 | 60.0 °C | |
| RTI Str | UL 746 | 60.0 °C | |
| ball-indentation hardness | EMAC | 80 °C | |
| RTI Elec | UL 746 | 60.0 °C |