Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.01 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.70to1.3 % |
| Shrinkage rate | | ISO294-4 | 0.60to0.90 % |
| Water absorption rate | | ISO62 | 1.0 % |
| viscosity number | | ISO307 | 190 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 40 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 80.0 MPa |
| Tensile stress | | ISO527-2 | 17.0 MPa |
| Tensile stress | | ISO527-2 | 9.50 MPa |
| Tensile strain | Break | ISO527-2 | >200 % |
| Tensile creep modulus | | ISO899-1 | 60.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+11 ohms·cm |
| dielectric strength | | IEC60243-1 | 35 kV/mm |
| | IEC60250 | 7.50 |
| | IEC60250 | 4.90 |
| Dissipation Factor | | IEC60250 | 0.070 |
| Dissipation Factor | | IEC60250 | 0.12 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 55.0 °C |
| vicat | | ISO306/A | 125 °C |
| vicat | | ISO306/B | 60.0 °C |
| | ISO11359-2 | 2.4E-04 cm/cm/°C |
| | ISO11359-2 | 2.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.