ABS POLYLAC® PA-777C CHI MEI CORPORATION

Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO 1183	1.06 g/cm³
melt mass-flow rate	ISO 1133	7.0 g/10min
Shrinkage rate	ISO 294-4	0.30to0.60 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Dart impact		ASTM D4226	9.00 J/cm
Dart impact	Dart impact		ASTM D4226	17.0 J/cm
Impact strength of cantilever beam gap		ISO 180/1A	9.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	18 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	44.0 MPa
tensile strength	tensile strength	Break	ISO 527-2/50	35.0 MPa
Tensile strain	Break	ISO 527-2/50	44 %
Flexural modulus		ISO 178	2200 MPa
bending strength		ISO 178	69.0 MPa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	92.0 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	112 °C
vicat		ISO 306/A50	119 °C
vicat	vicat		ISO 306/B50	112 °C
Linear coefficient of thermal expansion		ISO 11359-2	8.2E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.